Features and Benefits

Polyurethane winter gun foam


  • Excellent adhesion on most materials
  • High thermal and acoustical insulation
  • Accurate dosage
  • Low temperature application up to -10°C

Read More

CERESIT TS52 PRO WINTER is a one-component moisture cure semi-rigid polyurethane foam, with excellent cells structure and good mechanical strength. It is easily usable and specially made for application with an application gun. Product can be applied from temperatures up to –10°C. The foam is self-expanding and during the curing process expands about two times until cured, due to which some free space for expanding must be considered.  At minus temperatures the expansion of the foam is lower. Has excellent adhesion on wood, concrete, stone, metal etc.  Yield of the cured foam largely depends on working conditions - temperature, air humidity, available space for expanding, etc. Product does not contain CFC-propellants.

Step by step

Substrate preparation

  • Ensure substrates are stable, clean and free of substances likely to impair adhesion.
  • Moisturize mineral, porous substrates (brickwork, concrete, limestone) with water spray for enhanced adhesion.
  • Mask off adjacent areas with foil.
  • The application surfaces must be clean and free from dust. They can be moist, but not iced.

Can preparation

  • Application temperature (environment) of this product is -10°C to +30°C.
  • Recomended can temperature is +5 … +30 °C.
  • Store can preferably for at least 12 hours in room temperature.
  • Remove the plastic cap from the can and either screw the plastic pipe tightly onto the can or screw the can direct and tightly onto the can. Shake the can vigorously before use (15 - 20 times).


  • When working with the can always keep the can upside down (valve down).
  • Dosage is adjustable by pressing the trigger of the valve. Since the foam is expanding until cured, some free space for expanding should be left.
  • Dispense the foam sparingly to avoid excess overflows. Repeat shaking regularly during application.
  • Moisturising the surfaces and the foam improves adhesion and cured foam’s cellular structure.
  • If there are longer pauses than 5 to 10 minutes during working, the nozzle and valve must be cleaned using PU foam cleaner (e.g CERESIT CLEANER TS100).
  • Hardened foam can only be removed mechanically.


Limitations to joint maximal width exist in regard of ambient temperature and humidity levels. In dry conditions (during winter time, in rooms with central heating etc.), in order to get best foam structure and foam properties it is recommendable to fill gaps and joints in several layers by the application of smaller foam strings (up to 3 -4 cm thickness) and slightly moisturizing between every layer.